This paper investigates the time and temperature dependence of a ductile polymer, polypropylene, from the mechanical point of view. As the polymeric specimens have been manufactured by the injection molding process, the influence of mold temperature has been also subjected to the study. Compression tests have been performed both in quasi static and dynamic range ( 10–3/103 s−1), at different test temperatures (− 20/40 °C), and the results have been analysed in terms of yield stress and failure behaviour. The strength of the polymer is strongly influenced from all the input parameters. Mold temperature has a relevant effect only at room and high temperature. Polypropylene reveals a ductile to brittle transition when it is loaded at high rates, except when test temperature is high. The relation between test temperature, strain rate and yield stress is found to be well described by the Ree–Eyring model, adapted to the two relaxation mechanisms involved.

Investigation of the Effects of Mold Temperature, Test Temperature and Strain Rate on Mechanical Behaviour of Polypropylene

Mancini, E.;
2019-01-01

Abstract

This paper investigates the time and temperature dependence of a ductile polymer, polypropylene, from the mechanical point of view. As the polymeric specimens have been manufactured by the injection molding process, the influence of mold temperature has been also subjected to the study. Compression tests have been performed both in quasi static and dynamic range ( 10–3/103 s−1), at different test temperatures (− 20/40 °C), and the results have been analysed in terms of yield stress and failure behaviour. The strength of the polymer is strongly influenced from all the input parameters. Mold temperature has a relevant effect only at room and high temperature. Polypropylene reveals a ductile to brittle transition when it is loaded at high rates, except when test temperature is high. The relation between test temperature, strain rate and yield stress is found to be well described by the Ree–Eyring model, adapted to the two relaxation mechanisms involved.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11389/27952
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact